CHEN Bao-chun, LI Cong, HUANG Wei, AN Ming-zhe, HAN Song, DING Qing-jun. Review of ultra-high performance concrete shrinkage[J]. Journal of Traffic and Transportation Engineering, 2018, 18(1): 13-28. doi: 10.19818/j.cnki.1671-1637.2018.01.002
Citation: CHEN Bao-chun, LI Cong, HUANG Wei, AN Ming-zhe, HAN Song, DING Qing-jun. Review of ultra-high performance concrete shrinkage[J]. Journal of Traffic and Transportation Engineering, 2018, 18(1): 13-28. doi: 10.19818/j.cnki.1671-1637.2018.01.002

Review of ultra-high performance concrete shrinkage

doi: 10.19818/j.cnki.1671-1637.2018.01.002
More Information
  • Author Bio:

    CHEN Bao-chun(1958-), male, PhD, professor, baochunchen@fzu, edu.cn

  • Received Date: 2017-09-14
  • Publish Date: 2018-02-25
  • The shrinkage characteristics of ultra-high performance concrete (UHPC) were analyzed.The general rules of UHPC contraction with time were introduced.The influences of material composition, curing regime, internal temperature and internal humidity on UHPC shrinkage were summarized.Research result indicates that the shrinkage of UHPC develops rapidly at 0-7 d, accounting for 61.3%-86.5% of total shrinkage, develops slowly from 7 dto28 d, accounting for 13.5%-27.9%, and becomes steady after 28 d.Autogenic shrinkage is the main cause of early cracking of UHPC, and accounts for 78.6%-90.0% of total shrinkage.In term of the start point about shrinkage test, the initial time of test is 1 d (24 h) after specimen forming, and the termination time is 90 dor 120 d.In term of structural design, it may refer to the values (500-800με) in various countries' standards, and not to consider the residualshrinkage after heat curing.In term of shrinkage prediction models, the norms of all countries have not been uniformed yet, it can only refer to the existing models, and the shrinkage prediction models should be improved and revised.In term of component research, the quantitative impacts of types and contents of fibers and mineral admixtures on the shrinkage are research emphasis, the effect of each component on the shrinkage is different, and the evaluation indexes are relatively simple and should be combined with structural applications, preparation techniques and construction process to comprehensively evaluate the shrinkage.In term of the internal temperature and humidity fields, the research mainly concentrates on normal concretes, high-strength and high-performance concretes after 28 d, and it should be more in-depth study on the early internal temperature and humidity fields of UHPC with the large content of cementitious material, obvious difference of components, and high content of active mineral admixture.In term of reducing shrinkage, internal curing, expansive agent, shrinkage-reducing agent, coarse aggregate, and other measures are applied.Therefore, it should optimize the ratio of UHPC, rationalize the use of admixture, and adopt proper curing system and other measures to reduce the shrinkage of UHPC, but not to reduce its mechanical properties.

     

  • loading
  • [1]
    陈宝春, 季韬, 黄卿维, 等. 超高性能混凝土研究综述[J]. 建筑科学与工程学报, 2014, 31 (3): 1-24. doi: 10.3969/j.issn.1673-2049.2014.03.002

    CHEN Bao-chun, JI Tao, HUANG Qing-wei, et al. Review of research on ultra-high performance concrete[J]. Journal of Architecture and Civil Engineering, 2014, 31 (3): 1-24. (in Chinese). doi: 10.3969/j.issn.1673-2049.2014.03.002
    [2]
    林上顺, 黄卿维, 陈宝春, 等. 跨海大桥U-RC组合桥墩设计[J]. 交通运输工程学报, 2017, 17 (4): 55-65. doi: 10.3969/j.issn.1671-1637.2017.04.006

    LIN Shang-shun, HUANG Qing-wei, CHEN Bao-chun, et al. Design of U-RC composite pier of sea-crossing bridge[J]. Journal of Traffic and Transportation Engineering, 2017, 17 (4): 55-65. (in Chinese). doi: 10.3969/j.issn.1671-1637.2017.04.006
    [3]
    黄伟, 孙伟. 石灰石粉掺量对超高性能混凝土水化演变的影响[J]. 东南大学学报: 自然科学版, 2017, 47 (4): 751-759. https://www.cnki.com.cn/Article/CJFDTOTAL-DNDX201704020.htm

    HUANG Wei, SUN Wei. Effects of limestone addition on hydration development of ultra-high performance concrete[J]. Journal of Southeast University: Natural Science Edition, 2017, 47 (4): 751-759. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-DNDX201704020.htm
    [4]
    韩松, 刘丹, 张戈, 等. 超低水胶比复合胶凝材料孔结构随养护制度和龄期的变化机理[J]. 硅酸盐学报, 2017, 45 (11): 1594-1604. https://www.cnki.com.cn/Article/CJFDTOTAL-GXYB201711007.htm

    HAN Song, LIU Dan, ZHANG Ge, et al. Mechanism of curing effect on pore structure of hardened cementitious composites with ultra-low water to binder ratio[J]. Journal of the Chinese Ceramic Society, 2017, 45 (11): 1594-1604. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GXYB201711007.htm
    [5]
    张云升, 张国荣, 李司晨. 超高性能水泥基复合材料早期自收缩特性研究[J]. 建筑材料学报, 2014, 17 (1): 19-23. doi: 10.3969/j.issn.1007-9629.2014.01.004

    ZHANG Yun-sheng, ZHANG Guo-rong, LI Si-chen. Study on early autogenous shrinkage of ultra-high performance cementitous composite[J]. Journal of Building Materials, 2014, 17 (1): 19-23. (in Chinese). doi: 10.3969/j.issn.1007-9629.2014.01.004
    [6]
    缪昌文, 田倩, 刘加平, 等. 基于毛细管负压技术测试混凝土最早期的自干燥效应[J]. 硅酸盐学报, 2007, 35 (4): 509-516. doi: 10.3321/j.issn:0454-5648.2007.04.023

    MIAO Chang-wen, TIAN Qian, LIU Jia-ping, et al. Very early age self-desiccation effect measurement based on meniscus depression technology for concrete[J]. Journal of the Chinese Ceramic Society, 2007, 35 (4): 509-516. (in Chinese). doi: 10.3321/j.issn:0454-5648.2007.04.023
    [7]
    李家和, 刘铁军, 欧进萍. 高性能混凝土的自收缩与干燥收缩[C]//中国土木工程学会. 高强与高性能混凝土委员会第五届学术讨论会论文集. 北京: 中国土木工程学会, 2004: 77-82.

    LI Jia-he, LIU Tie-jun, OU Jin-ping. Autogenous shrinkage and dry shrinkage of high performance concrete[C]//China Civil Engineering Society. Proceedings of the fifth symposium of High Strength and High Performance Concrete Committee. Beijing: China Civil Engineering Society, 2004: 77-82. (in Chinese).
    [8]
    赖秀英. 钢管混凝土拱桥收缩、徐变效应研究[D]. 福州: 福州大学, 2015.

    LAI Xiu-ying. Research on effects of shrinkage and creep in concrete filled steel tubular arch bridges[D]. Fuzhou: Fuzhou University, 2015. (in Chinese).
    [9]
    安明喆, 朱金铨, 覃维祖. 高性能混凝土的自收缩问题[J]. 建筑材料学报, 2001, 4 (2): 159-166. doi: 10.3969/j.issn.1007-9629.2001.02.012

    AN Ming-zhe, ZHU Jin-quan, QIN Wei-zu. Autogenous shrinkage of high performance concrete[J]. Journal of Building Materials, 2001, 4 (2): 159-166. (in Chinese). doi: 10.3969/j.issn.1007-9629.2001.02.012
    [10]
    VANDE VOORT T L, SULEIMAN M T, SRITHARAN S. Design and performance verification of ultra-high performance concrete piles for deep foundations[R]. Ames: Iowa State University, 2008.
    [11]
    王国杰. 自密实混凝土圆环约束收缩试验研究[J]. 工程力学, 2014, 31 (12): 173-180. doi: 10.6052/j.issn.1000-4750.2014.10.0833

    WANG Guo-jie. Experimental study on restrained shrinkage of self-compacting concrete by ring test[J]. Engineering Mechanics, 2014, 31 (12): 173-180. (in Chinese). doi: 10.6052/j.issn.1000-4750.2014.10.0833
    [12]
    VOGT C, LAGERBLAD B, PERSSON T H. Optimization of UHPC for selective stabilization of deep boreholes[C]//SCHMIDT M, FEHLING E, GEISENHANSLÜKE C. 1st International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2004: 769-781.
    [13]
    GRAYBEAL B A. Material property characterization of ultrahigh performance concrete[R]. Washington DC: Federal Highway Administration, 2006.
    [14]
    FEHLING E, SCHMIDT M, TEICHMANN T, et al. Entwicklung, dauerhaftigkeit und berechnung ultrahochfester betone (UHPC)[R]. Kassel: Kassel University Press, 2005.
    [15]
    DELPLACE G, HAJAR Z, SIMON A. Precast thin shells made of UHPFRC for a large roof in a wastewater treatment plant near Paris[C]//SCHMIDT M, FEHLING E, GLOTZBACH C, et al. 3rd International Symposium on UHPC and Nanotechnology for High Performance Construction Materials. Kassel: Kassel University Press, 2012: 1011-1018.
    [16]
    LI Cong, LUO Xia, CHEN Bao-chun, et al. Experimental on shrinkage performance of ultra high performance concrete under sealed condition[C]//SHI Cai-jun, DENG Lu, GONG Jian-qing, et al. 1st International Conference on UHPC Materials and Structures. New York: RILEM Publications, 2016: 420-429.
    [17]
    MAEDER U, LALLEMANT-GAMBOA I, CHAIGNON J, et al. Ceracem, a new high performance concrete: characterisations and applications[C]//SCHMIDT M, FEHLING E, GEISENHANSLÜKE C. 1st International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2004: 59-68.
    [18]
    SOLIMAN A M. Early-age shrinkage of ultra high-performance concrete: mitigation and compensating mechanisms[D]. London: The University of Western Ontario, 2011.
    [19]
    GRAYBEAL B A. Characterization of the behavior of ultrahigh performance concrete[D]. College Park: University of Maryland, 2005.
    [20]
    赵筠, 廉慧珍, 金建昌. 钢-混凝土复合的新模式——超高性能混凝土(UHPC/UHPFRC): 收缩与裂缝, 耐高温性能, 渗透性与耐久性, 设计指南[J]. 混凝土世界, 2013 (12): 60-71. https://www.cnki.com.cn/Article/CJFDTOTAL-JZSJ201312010.htm

    ZHAO Jun, LIAN Hui-zhen, JIN Jian-chang. A new model of steel-concrete composite-ultra-high performance concrete (UHPC/UHPFRC): shrinkage and cracking, high temperature performance, permeability and durability and design guide[J]. China Concrete, 2013 (12): 60-71. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-JZSJ201312010.htm
    [21]
    STAQUET S, BOULAY C, D'ALOÏA L, et al. Autogenous shrinkage of a self-compacting VHPC in isothermal and realistic temperature conditions[C]//MARCHAND J, BISSONNETTE B, GAGNÉR, et al. 2nd International Symposium on Advances in Concrete through Science and Engineering. Bagneux: RILEM Publications, 2006: 1-5.
    [22]
    SHINK M, VACHER J P. EFFIX design?—properties and applications of a creative concrete[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 847-854.
    [23]
    HABEL K, CHARRON J P, DENARIÉE, et al. Autogenous deformations and viscoelasticity of UHPFRC in structures. Part I: Experimental results[J]. Magazine of Concrete Research, 2006, 58 (3): 135-145. doi: 10.1680/macr.2006.58.3.135
    [24]
    赵筠, 廉慧珍, 金建昌. 钢-混凝土复合的新模式——超高性能混凝土(UHPC/UHPFRC): 钢-混凝土复合模式的现状、问题及对策与UHPC发展历程[J]. 混凝土世界, 2013 (10): 56-69. doi: 10.3969/j.issn.1674-7011.2013.10.010

    ZHAO Jun, LIAN Hui-zhen, JIN Jian-chang. A new model of steel-concrete composite-ultra-high performance concrete (UHPC/UHPFRC): present situation, problems and countermeasures of steel-concrete composite structure and the development of UHPC[J]. China Concrete, 2013 (10): 56-69. (in Chinese). doi: 10.3969/j.issn.1674-7011.2013.10.010
    [25]
    胡功球. 不同养护条件下超高性能混凝土(UHPC) 的收缩性能研究[D]. 长沙: 湖南大学, 2015.

    HU Gong-qiu. Research on the shrinkage performance of ultra high performance concrete under different curing condition[D]. Changsha: Hunan University, 2015. (in Chinese).
    [26]
    曹世勇. 超高性能水泥基复合材料自收缩特性及其机理研究[J]. 硅酸盐通报, 2015, 34 (3): 813-818, 823. https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201503048.htm

    CAO Shi-yong. Study on autogenous shrinkage characteristic and mechanism of ultra-high performance cementitous composite[J]. Bulletin of the Chinese Ceramic Society, 2015, 34 (3): 813-818, 823. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201503048.htm
    [27]
    KOH K, RYU G S, KANG S, et al. Shrinkage properties of ultra-high performance concrete (UHPC)[J]. Journal of Computational and Theoretical Nanoscience, 2011, 4 (3): 948-952.
    [28]
    WONG A C L, CHILDS P A, BERNDT R, et al. Simultaneous measurement of shrinkage and temperature of reactive powder concrete at early-age using fibre Bragg grating sensors[J]. Cement and Concrete Composites, 2007, 29 (6): 490-497. doi: 10.1016/j.cemconcomp.2007.02.003
    [29]
    刘丹. 不同养护制度下活性粉末混凝土早期收缩的模型研究[D]. 北京: 北京交通大学, 2018.

    LIU Dan. Research on the early-age shrinkage model of reactive powder concrete in different curing conditions[D]. Beijing: Beijing Jiaotong University, 2018. (in Chinese).
    [30]
    丁庆军, 陈凯, 徐敏, 等. 掺钢渣粉四元复合体系RPC的制备及其体积变形[C]//中国硅酸盐学会. 2009中国商品混凝土可持续发展论坛暨第六届全国商品混凝土技术与管理交流大会论文集. 北京: 中国硅酸盐学会, 2009: 16-20.

    DING Qing-jun, CHEN Kai, XU Min, et al. Research the performance of the quarter composite system of RPC with steel slag powder[C]//Chinese Ceramic Society. 2009Proceedings of China Commodity Concrete Sustainable Development Forum and the 6th National Commodity Concrete Technology and Management Exchange Conference. Beijing: Chinese Ceramic Society, 2009: 16-20. (in Chinese).
    [31]
    宋正林. 天然硅质掺合料活性粉末混凝土研究[D]. 武汉: 武汉理工大学, 2011.

    SONG Zheng-lin. Study on reactive powder concrete with natural siliceous admixture[D]. Wuhan: Wuhan University of Technology, 2011. (in Chinese).
    [32]
    国爱丽, 赵福君, 巴恒静, 等. 活性粉末混凝土配比优化及收缩性能研究[J]. 武汉理工大学学报, 2009, 31 (2): 20-24. doi: 10.3963/j.issn.1671-4431.2009.02.006

    GUO Ai-li, ZHAO Fu-jun, BA Heng-jing, et al. Research on the mix optimization and shrinkage properties of reactive powder concrete[J]. Journal of Wuhan University of Technology, 2009, 31 (2): 20-24. (in Chinese). doi: 10.3963/j.issn.1671-4431.2009.02.006
    [33]
    LOUKILI A, KHELIDJ A, RICHARD P. Hydration kinetics, change of relative humidity, and autogenous shrinkage of ultrahigh-strength concrete[J]. Cement and Concrete Research, 1999, 29 (4): 577-584. doi: 10.1016/S0008-8846(99)00022-8
    [34]
    MAGUREANU C, NEGRUTIU C, HEGHES B, et al. Creep and shrinkage of high performance concrete[C]//SOHRAB S H, CATRAKIS H J, KOBASKO N. 7th IASME/WSEAS International Conference on Heat Transfer, Thermal Engineering and Environment. Moscow: WSEAS Press, 2009: 204-208.
    [35]
    KIM B S, KIM S, KIM Y J, et al. R and D activities and application of ultra high performance concrete to cable stayed bridges[C]//SCHMIDT M, FEHLING E, GLOTZBACH C, et al. 3rd International Symposium on UHPC and Nanotechnology for High Performance Construction Materials. Kassel: Kassel University Press, 2012: 865-872.
    [36]
    ACKER P, BEHLOUL M. Ductal® technology: a large spectrum of poperties, a wide range of applications[C]//SCHMIDT M, FEHLING E, GEISENHANSLÜKE C. 1st International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2004: 11-22.
    [37]
    REICHEL M, SPAROWITZ L, FREYTAG B. UHPC-segmental bridges—material-based design principles and adapted construction methods[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 779-786.
    [38]
    BURKART I, MÜLLER H S. Creep and shrinkage characteristics of ultra high strength concrete (UHPC)[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 469-476.
    [39]
    BURKART I, MÜLLER H S. Creep and shrinkage characteristics of ultra high strength concrete (UHPC)[C]//TANABE T, SAKATA K, MIHASHI H, et al. 8th International Conference on Creep, Shrinkage and Durability Mechanics of Concrete and Concrete Structures. Boca Raton: CRC Press, 2008: 469-476.
    [40]
    SOLIMAN A M, NEHDI M L. Effect of drying conditions on autogenous shrinkage in ultra-high performance concrete at earlyage[J]. Materials and Structures, 2011, 44 (5): 879-899. doi: 10.1617/s11527-010-9670-0
    [41]
    LUO Xia, CHEN Bao-chun, WEI Jian-gang, et al. Experimental study on shrinkage of sealed UHPC[C]//FEHLING E, MIDDENDORF B, THIEMICKE J. 4th International Symposium on Ultra High Performance Concrete and High Performance Construction Materials. Kassel: Kassel University Press, 2016: 1-9.
    [42]
    MÜLLER H S, ANDERS I. Creep and shrinkage characteristics of ultra-high performance concrete[C]//Asian Concrete Society. 1st International Symposium of Asian Concrete Federation on UHPC. Qishan: Asian Concrete Society, 2015: 51-59.
    [43]
    刘泰松. 活性粉末混凝土的收缩理论和试验研究[D]. 北京: 北京交通大学, 2007.

    LIU Tai-song. Shrinkage theory and experimental research of reactive powder concrete[D]. Beijing: Beijing Jiaotong University, 2007. (in Chinese).
    [44]
    KOENDERS E A B, VAN BREUGEL K. Numerical modelling of autogenous shrinkage of hardening cement paste[J]. Cement and Concrete Research, 1997, 27 (10): 1489-1499. doi: 10.1016/S0008-8846(97)00170-1
    [45]
    陈宝春, 赖秀英. 钢管混凝土收缩变形与钢管混凝土拱收缩应力[J]. 铁道学报, 2016, 38 (2): 112-123. doi: 10.3969/j.issn.1001-8360.2016.02.015

    CHEN Bao-chun, LAI Xiu-ying. Shrinkage deformation of concrete filled steel tube and shrinkage stress of concrete filled steel tubular arch[J]. Journal of the China Railway Society, 2016, 38 (2): 112-123. (in Chinese). doi: 10.3969/j.issn.1001-8360.2016.02.015
    [46]
    BAZANT Z P. RILEM draft recommendation: TC-242-MDC multi-decade creep and shrinkage of concrete: material model and structural analysis[J]. Materials and Structures, 2015, 48 (4): 753-770. doi: 10.1617/s11527-014-0485-2
    [47]
    HUBLER M H, WENDNER R, BAZANT Z P. Statistical justification of Model B4for drying and autogenous shrinkage of concrete and comparisons to other models[J]. Materials and Structures, 2015, 48 (4): 797-814. doi: 10.1617/s11527-014-0516-z
    [48]
    IPEK M, YILMAZ K, UYSAL M. The effect of pre-setting pressure applied flexural strength and fracture toughness of reactive powder concrete during the setting phase[J]. Construction and Building Materials, 2012, 26 (1): 459-465. doi: 10.1016/j.conbuildmat.2011.06.045
    [49]
    FEHLING E, SCHMIDT M, WALRAVEN J, et al. UltraHigh Performance Concrete UHPC: Fundamentals, Design, Examples[M]. Hoboken: Wiley, 2014.
    [50]
    涂亚秋. 活性粉末混凝土收缩影响因素的研究[D]. 北京: 北京交通大学, 2015.

    TU Ya-qiu. Research on the Influence factors for the shinkage of reactive powder concrete[D]. Beijing: Beijing Jiaotong University, 2015. (in Chinese).
    [51]
    黄政宇, 胡功球. 热养护过程中超高性能混凝土的收缩性能研究[J]. 材料导报, 2016, 30 (4): 115-120. https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201604030.htm

    HUANG Zheng-yu, HU Gong-qiu. Study on the shrinkage performance of ultra high performance concrete during heat curing[J]. Materials Review, 2016, 30 (4): 115-120. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201604030.htm
    [52]
    LURA P. Autogenous deformation and internal curing of concrete[D]. Delft: Delft University of Technical, 2003.
    [53]
    陈广智, 孟世强, 阎培渝. 养护条件和配合比对活性粉末混凝土变形率的影响[J]. 工业建筑, 2003, 33 (9): 63-65, 84. doi: 10.3321/j.issn:1000-8993.2003.09.020

    CHEN Guang-zhi, MENG Shi-qiang, YAN Pei-yu. Effects of curing condition and proportion ratio on reactive powder concrete[J]. Industrial Construction, 2003, 33 (9): 63-65, 84. (in Chinese). doi: 10.3321/j.issn:1000-8993.2003.09.020
    [54]
    FEHLING E, BUNJE K, SCHMIDT M, et al. The"gärtnerplatzbrücke"design of first hybrid UHPC-steel bridge across the River Fulda in Kassel, Germany[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 581-588.
    [55]
    SAGMEISTER B. On the way to micrometer scale: applications of UHPC in machinery construction[C]//SCHMIDT M, FEHLING E, GLOTZBACH C, et al. 3rd International Symposium on UHPC and Nanotechnology for High Performance Construction Materials. Kassel: Kassel University Press, 2012: 819-823.
    [56]
    LOUKILI A, CHOPIN D, KHELIDJ A, et al. A new approach to determine autogenous shrinkage of mortar at an early age considering temperature history[J]. Cement and Concrete Research, 2000, 30 (6): 915-922. doi: 10.1016/S0008-8846(00)00241-6
    [57]
    SLATNICK S, RIDING K A, FOLLIARD K J, et al. Evaluation of autogenous deformation of concrete at early ages[J]. ACI Materials Journal, 2011, 108 (1): 21-28.
    [58]
    韩松, 涂亚秋, 安明喆, 等. 活性粉末混凝土早期收缩规律及其控制方法[J]. 中国铁道科学, 2015, 36 (1): 40-47. doi: 10.3969/j.issn.1001-4632.2015.01.06

    HAN Song, TU Ya-qiu, AN Ming-zhe, et al. The shrinkage of reactive powder concrete in early age and its control methods[J]. China Railway Science, 2015, 36 (1): 40-47. (in Chinese). doi: 10.3969/j.issn.1001-4632.2015.01.06
    [59]
    MATSUBARA N, OHNO T, SAKAI G, et al. Application of a new type of ultra high strength fiber reinforced concrete to a prestressed concrete bridge[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 787-792.
    [60]
    TAZAWA E I, MIYAZAWA S. Experimental study on mechanism of autogenous shrinkage of concrete[J]. Cement and Concrete Research, 1995, 25 (8): 1633-1638. doi: 10.1016/0008-8846(95)00159-X
    [61]
    RADOCEA A. Autogenous volume change of concrete at very early age[J]. Magazine of Concrete Research, 1998, 50 (2): 107-113. doi: 10.1680/macr.1998.50.2.107
    [62]
    JENSEN O M, HANSEN P F. Water-entrained cement-based materials—I. Principles and theoretical background[J]. Cement and Concrete Research, 2001, 31 (4): 647-654. doi: 10.1016/S0008-8846(01)00463-X
    [63]
    高燕, 吕淑珍, 卢忠远, 等. 掺固硫灰活性粉末混凝土的制备和性能[J]. 材料研究学报, 2014, 28 (1): 59-66. https://www.cnki.com.cn/Article/CJFDTOTAL-CYJB201401008.htm

    GAO Yan, LU Shu-zhen, LU Zhong-yuan, et al. Preparation and properties of reactive powder concrete with circulating fluidized bed combustion fly ash[J]. Chinese Journal of Materials Research, 2014, 28 (1): 59-66. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-CYJB201401008.htm
    [64]
    ZHANG M H, TAM C T, LEOW M P. Effect of water-tocementitious materials ratio and silica fume on the autogenous shrinkage of concrete[J]. Cement and Concrete Research, 2003, 33 (10): 1687-1694. doi: 10.1016/S0008-8846(03)00149-2
    [65]
    冯浩. 超高性能混凝土早期塑性收缩开裂的研究[D]. 长沙: 湖南大学, 2014.

    FENG Hao. Study on early stage plastic shrinkage and cracking performance of ultra high performance concrete[D]. Changsha: Hunan University, 2014. (in Chinese).
    [66]
    JENSEN O M, HANSEN P F. Autogenous relative humidity change in silica fume-modified cement paste[J]. Advances in Cement Research, 1995, 7 (25): 33-38. doi: 10.1680/adcr.1995.7.25.33
    [67]
    LOBO C, COHEN M D. Effects of silica fume on expansion characteristics of expansive cement pastes[J]. ACI Materials Journal, 1992, 89 (5): 481-490.
    [68]
    RAO G A. Influence of silica fume replacement of cement on expansion and drying shrinkage[J]. Cement and Concrete Research, 1998, 28 (10): 1505-1509. doi: 10.1016/S0008-8846(98)00127-6
    [69]
    龙广成, 陈瑜. RPC200的强度及收缩影响研究[J]. 工业建筑, 2002, 32 (6): 4-7. doi: 10.3321/j.issn:1000-8993.2002.06.002

    LONG Guang-cheng, CHEN Yu. Study on the effect of factors on strength and shrinkage of RPC200[J]. Industrial Construction, 2002, 32 (6): 4-7. (in Chinese). doi: 10.3321/j.issn:1000-8993.2002.06.002
    [70]
    OESTERLEE C, SADOUKI H, BRZHWILER E. Structural analysis of a composite bridge girder combining UHPFRC and reinforced concrete[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 647-654.
    [71]
    KAMEN A. Comportement au jeune age et différéd'un BFUPécrouissant sous les effets thermomécaniques[D]. Oran: University of Science and Tecnology of Oran, 2007.
    [72]
    施韬. 掺矿渣活性粉末混凝土及其高耐久性的研究[D]. 杭州: 浙江工业大学, 2004.

    SHI Tao. Study on the ractive powder concrete with blastfurnace slag and it's high durabilities[D]. Hangzhou: Zhejiang University of Technology, 2004. (in Chinese).
    [73]
    吴林妹, 史才军, 张祖华, 等. 钢纤维对超高性能混凝土干燥收缩的影响[J]. 材料导报, 2017, 31 (12): 58-65. https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201723007.htm

    WU Lin-mei, SHI Cai-jun, ZHANG Zu-hua, et al. Effects of steel fiber on drying shrinkage of ultra high performance concrete[J]. Materials Review, 2017, 31 (12): 58-65. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201723007.htm
    [74]
    HANNAWI K, BIAN Hui, PRINCE-AGBODJAN W, et al. Effect of different types of fibers on the microstructure and the mechanical behavior of ultra-high performance fiberreinforced Concretes[J]. Composites Part B: Engineering, 2016, 86: 214-220. doi: 10.1016/j.compositesb.2015.09.059
    [75]
    TERZIJSKI I. Optimization of UHPC for the model of a pedestrian bridge[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 707-714.
    [76]
    ORGASS M, KLUG Y. Fibre reinforced ultra-high strength concretes[C]//SCHMIDT M, FEHLING E, GEISENHANSLÜKE C. 1st International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2004: 637-647.
    [77]
    GARAS V Y, KAHN L F, KURTIS K E. Short-term tensile creep and shrinkage of ultra-high performance concrete[J]. Cement and Concrete Composites, 2009, 31 (3): 147-152. doi: 10.1016/j.cemconcomp.2009.01.002
    [78]
    SOLIMAN A M, NEHDI M L. Effect of natural wollastonite microfibers on early-age behavior of UHPC[J]. Journal of Materials in Civil Engineering, 2012, 24 (7): 816-824. doi: 10.1061/(ASCE)MT.1943-5533.0000473
    [79]
    SOLIMAN A M, NEHDI M L. Effects of shrinkage reducing admixture and wollastonite microfiber on early-age behavior of ultra-high performance concrete[J]. Cement and Concrete Composites, 2014, 46: 81-89. doi: 10.1016/j.cemconcomp.2013.11.008
    [80]
    STAQUET S, ESPION B. Early-age autogenous shrinkage of UHPC incorporating very fine fly ash or metakaolin in replacement of silica fume[C]//SCHMIDT M, FEHLING E, GEISENHANSLÜKE C. 1st International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2004: 587-599.
    [81]
    MARQUEZ S, HANSON S, TIKALSKY P J. Environmental advantages of ternary cement combinations[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 135-141.
    [82]
    KIM Jin-keun, LEE Chil-sung. Moisture diffusion of concrete considering self-desiccation at early ages[J]. Cement and Concrete Research, 1999, 29 (12): 1921-1927. doi: 10.1016/S0008-8846(99)00192-1
    [83]
    蒋正武, 王培铭. 等温干燥条件下混凝土内部相对湿度的分布[J]. 武汉理工大学学报, 2003, 25 (7): 18-21. doi: 10.3321/j.issn:1671-4431.2003.07.006

    JIANG Zheng-wu, WANG Pei-ming. Internal relative humidity distribution of concrete under isothermal and dry conditions[J]. Journal of Wuhan University of Technology, 2003, 25 (7): 18-21. (in Chinese). doi: 10.3321/j.issn:1671-4431.2003.07.006
    [84]
    KAMEN A, DENARIE E, SADOUKI H, et al. Thermomechanical response of UHPFRC at early age—experimental study and numerical simulation[J]. Cement and Concrete Research, 2008, 38 (6): 822-831. doi: 10.1016/j.cemconres.2008.01.009
    [85]
    SCHEYDT J C, MÜLLER H S. Microstructure of ultra high performance concrete (UHPC) and its impact on durability[C]//SCHMIDT M, FEHLING E, GLOTZBACH C, et al. 3rd International Symposium on UHPC and Nanotechnology for High Performance Construction Materials. Kassel: Kassel University Press, 2012: 349-356.
    [86]
    BAZANT Z P, NAJJAR L J. Nonlinear water diffusion in nonsaturated concrete[J]. Matériaux et Construction, 1972, 5 (1): 3-20. doi: 10.1007/BF02479073
    [87]
    黄瑜, 祁锟, 张君. 早龄期混凝土内部湿度发展特征[J]. 清华大学学报: 自然科学版, 2007, 47 (3): 309-312. doi: 10.3321/j.issn:1000-0054.2007.03.003

    HUANG Yu, QI Kun, ZHANG Jun. Development of internal humidity in concrete at early ages[J]. Journal of Tsinghua University: Science and Technology, 2007, 47 (3): 309-312. (in Chinese). doi: 10.3321/j.issn:1000-0054.2007.03.003
    [88]
    高原, 张君, 孙伟. 干湿循环下混凝土湿度与变形的测量[J]. 清华大学学报: 自然科学版, 2012, 52 (2): 144-149. https://www.cnki.com.cn/Article/CJFDTOTAL-QHXB201202003.htm

    GAO Yuan, ZHANG Jun, SUN Wei. Concrete deformation and interior humidity during dry-wet cycles[J]. Journal of Tsinghua University: Science and Technology, 2012, 52 (2): 144-149. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-QHXB201202003.htm
    [89]
    高原, 张君, 韩宇栋. 干湿交替下混凝土内部相对湿度变化规律[J]. 建筑材料学报, 2013, 16 (3): 375-381. doi: 10.3969/j.issn.1007-9629.2013.03.001

    GAO Yuan, ZHANG Jun, HAN Yu-Dong. Experimental study on the internal relative humidity in conctete under drywet cycles[J]. Journal of Building Materials, 2013, 16 (3): 375-381. (in Chinese). doi: 10.3969/j.issn.1007-9629.2013.03.001
    [90]
    ANDRADE C, SARRIA J, ALONSO C. Relative humidity in the interior of concrete exposed to natural and artificial weathering[J]. Cement and Concrete Research, 1999, 29 (8): 1249-1259. doi: 10.1016/S0008-8846(99)00123-4
    [91]
    PARROTT L J. Some effects of cement and curing upon carbonation and reinforcement corrosion in concret[J]. Materials and Structures, 1996, 29 (187): 164-173.
    [92]
    NILSSON L O. Long-term moisture transport in high performance concrete[J]. Materials and Structures, 2002, 35 (254): 641-649. doi: 10.1617/13972
    [93]
    BENTZ D P. A review of early-age properties of cementbased materials[J]. Cement and Concrete Research, 2008, 38 (2): 196-204.
    [94]
    AYANO T, WITTMANN F H. Drying, moisture distribution, and shrinkage of cement-based materials[J]. Materials and Structures, 2002, 34 (247): 134-140.
    [95]
    GRASLEY Z C, LANGE D A. Thermal dilation and internal relative humidity of hardened cement paste[J]. Materials and Structures, 2007, 40 (3): 311-317.
    [96]
    PERSSON B. Moisture in concrete subjected to different kinds of curing[J]. Materials and Structures, 1997, 30 (203): 533-544.
    [97]
    周继凯, 慕建磊, 严媛媛, 等. 早龄期混凝土内部湿度场的测量与数值模拟[J]. 科学技术与工程, 2013, 13 (15): 4252-4256. https://www.cnki.com.cn/Article/CJFDTOTAL-KXJS201315020.htm

    ZHOU Ji-kai, MU Jian-lei, YAN Yuan-yuan, et al. Measurement and numerical simulation of internal humidity field in earlyage concrete[J]. Science Technology and Engineering, 2013, 13 (15): 4252-4256. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-KXJS201315020.htm
    [98]
    HUA C, ACKER P, EHRLACHER A. Analyses and models of the autogenous shrinkage of hardening cement paste—I. Modelling at macroscopic scale[J]. Cement and Concrete Research, 1995, 25 (7): 1457-1468.
    [99]
    KOENDERS E A B, VAN BREUGEL K. Numerical modelling of autogenous shrinkage of hardening cement paste[J]. Cement and Concrete Research, 1997, 27 (10): 1489-1499.
    [100]
    HUA C, EHRLACHER A, ACKER P. Analyses and models of the autogenous shrinkage of hardening cement paste—II. Modelling at scale of hydrating grains[J]. Cement and Concrete Research, 1997, 27 (2): 245-258.
    [101]
    王建, 戴会超, 顾冲时. 混凝土湿度运移数值计算综述[J]. 水力发电学报, 2005, 24 (2): 85-89. https://www.cnki.com.cn/Article/CJFDTOTAL-SFXB200502020.htm

    WANG Jian, DAI Hui-chao, GU Chong-shi. Summary on numerical calculation of moisture transfer in concrete[J]. Journal of Hydroelectric Engineering, 2005, 24 (2): 85-89. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-SFXB200502020.htm
    [102]
    耿飞, 钱春香, 樊建平. 纤维和膨胀剂对混凝土收缩性能的影响[J]. 混凝土与水泥制品, 2003 (5): 33-35. https://www.cnki.com.cn/Article/CJFDTOTAL-HNTW200305011.htm

    GENG Fei, QIAN Chun-xiang, FAN Jian-ping. Effects of fiber and expansive agent on shrinkage performance of concrete[J]. China Concrete and Cement Products, 2003 (5): 33-35. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-HNTW200305011.htm
    [103]
    王勇威. 超高强高性能混凝土的组成、结构及其收缩与补偿的研究[D]. 重庆: 重庆大学, 2001.

    WANG Yong-wei. Composition, structure, shrinkage and compensation of ultra-high performance concrete[D]. Chongqing: Chongqing University, 2001. (in Chinese).
    [104]
    赵顺增, 刘立, 郑万廪, 等. 高性能补偿收缩混凝土用膨胀剂—HCSA的特点及其应用[J]. 膨胀剂与膨胀混凝土, 2009 (2): 2-5. https://cpfd.cnki.com.cn/Article/CPFDTOTAL-EUGQ200902002004.htm

    ZHAO Shun-Zeng, LIU Li, ZHENG Wan-lin, et al. Characteristics and applications of expansive agent—HCSA for high performance compensating shrinkage concrete[J]. Expansive Agents and Expansive Concrete, 2009 (2): 2-5. (in Chinese). https://cpfd.cnki.com.cn/Article/CPFDTOTAL-EUGQ200902002004.htm
    [105]
    赵顺增, 刘立, 郑万廪, 等. HCSA双膨胀源高性能混凝土膨胀剂[J]. 膨胀剂与膨胀混凝土, 2016 (1): 1-5, 16. https://www.cnki.net/KCMS/detail/detail.aspx?dbcode=IPFD&filename=EUGQ200509007002&dbname=IPFD9914

    ZHAO Shun-Zeng, LIU Li, ZHENG Wan-lin, et al. HCSA double expansive sources high performance concrete expanding agent[J]. Expansive Agents and Expansive Concrete, 2016 (1): 1-5, 16. (in Chinese). https://www.cnki.net/KCMS/detail/detail.aspx?dbcode=IPFD&filename=EUGQ200509007002&dbname=IPFD9914
    [106]
    黄政宇, 刘永强, 李操旺. 掺HCSA膨胀剂超高性能混凝土性能的研究[J]. 材料导报, 2015, 29 (2): 116-121. https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201504029.htm

    HUANG Zheng-yu, LIU Yong-qiang, LI Cao-wang. Performance research of ultra high performance concrete incorporating HCSA expansion agent[J]. Materials Review, 2015, 29 (2): 116-121. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201504029.htm
    [107]
    GAGNÉR. Shrinkage-reducing admixtures[J]. Science and Technology of Concrete Admixtures, 2015: 457-469.
    [108]
    刘加平, 田倩, 唐明述. 膨胀剂和减缩剂对于高性能混凝土收缩开裂的影响[J]. 东南大学学报: 自然科学版, 2006, 36 (增2): 195-199. https://www.cnki.com.cn/Article/CJFDTOTAL-DNDX2006S2036.htm

    LIU Jia-ping, TIAN Qian, TANG Ming-shu. Influence of expansion agent and shrinkage reducing agent on shrinkage cracking of high performance concrete[J]. Journal of Southeast University: Natural Science Edition, 2006, 36 (S2): 195-199. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-DNDX2006S2036.htm
    [109]
    PARK Jung-jun, YOO Doo-yeol, KIM Sung-wook, et al. Drying shrinkage cracking characteristics of ultra-high performance fibre reinforced concrete with expansive and shrinkage reducing agents[J]. Magazine of Concrete Research, 2013, 65 (4): 248-256.
    [110]
    MALTESE C, PISTOLESI C, LOLLI A, et al. Combined effect of expansive and shrinkage reducing admixtures to obtain stable and durable mortars[J]. Cement and Concrete Research, 2005, 35 (12): 2244-2251.
    [111]
    MARUYAMA I, ITO H, SATO R. Expansive behavior of expansive high strength concrete and its induced stress[C]//SCHMIDT M, FEHLING E, GEISENHANSLÜKE C. 1st International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2004: 601-613.
    [112]
    PARK Jung-jun, YOO Doo-yeol, KIM Sung-wook, et al. Benefits of using expansive and shrinkage-reducing agents in UHPC for volume stability[J]. Magazine of Concrete Research, 2014, 66 (14): 745-750.
    [113]
    PARK Jung-jun, YOO Doo-yeol, KIM Sung-wook, et al. Autogenous shrinkage of ultra high performance concrete considering early age coefficient of thermal expansion[J]. Structural Engineering and Mechanics, 2014, 49 (6): 763-773.
    [114]
    黄卿维, 沈秀将, 陈宝春, 等. 韩国超高性能混凝土桥梁研究与应用[J]. 中外公路, 2016, 36 (2): 222-225. https://www.cnki.com.cn/Article/CJFDTOTAL-GWGL201602050.htm

    HUANG Qing-wei, SHEN Xiu-jiang, CHEN Bao-chun, et al. Research and application of ultra-high performance concrete bridge in Korea[J]. Journal of China and Foreign Highway, 2016, 36 (2): 222-225. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GWGL201602050.htm
    [115]
    KIM Sung-wook, PARK Jung-jun, YOO Doo-yeol, et al. Shrinkage behavior of ultra high performance concrete at the manufacturing stage[C]//SCHMIDT M, FEHLING E, GLOTZBACH C, et al. 3rd International Symposium on UHPC and Nanotechnology for High Performance Construction Materials. Kassel: Kassel University Press, 2012: 317-324.
    [116]
    DUDZIAK L, MECHTCHERINE V. Mitigation of volume changes of ultra-high performance concrete (UHPC) by using super absorbent polymers[C]//FEHLING E, SCHMIDT M, STÜRWALD S. 2nd International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2008: 425-432.
    [117]
    JENSEN O M, LURA P. Materials and methods for internal curing[R]. New York: Curran Associates, 2007.
    [118]
    VAN TUAN N, YE Guang, VAN BREUGEL K. Mitigation of early age shrinkage of ultra high performance concrete by using rice husk ash[C]//SCHMIDT M, FEHLING E, GLOTZBACH C, et al. 3rd International Symposium on UHPC and Nanotechnology for High Performance Construction Materials. Kassel: Kassel University Press, 2012: 341-348.
    [119]
    叶光, NGUYEN V T. 稻壳灰抑制超高性能混凝土的自收缩机理分析[J]. 硅酸盐学报, 2012, 40 (2): 212-216. https://www.cnki.com.cn/Article/CJFDTOTAL-GXYB201202008.htm

    YE Guang, NGUYEN V T. Mitigation of autogenous shrinkage of ultra-high performance concrete by rice husk ash[J]. Journal of the Chinese Ceramic Society, 2012, 40 (2): 212-216. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GXYB201202008.htm
    [120]
    DUDZIAK L. Mitigating autogenous shrinkage of ultra-high performance concrete by means of internal curing using superabsorbent polymers[D]. Dresden: Technische Universität Dresden, 2016.
    [121]
    黄政宇, 王嘉. 高吸水性树脂对超高性能混凝土性能的影响[J]. 硅酸盐通报, 2012, 31 (3): 539-544. https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201203010.htm

    HUANG Zheng-yu, WANG Jia. Effects of SAP on the performance of UHPC[J]. Bulletin of the Chinese Ceramic Society, 2012, 31 (3): 539-544. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201203010.htm
    [122]
    CRAEYE B, GEIRNAERT M, SCHUTTER G D. Super absorbing polymers as an internal curing agent for mitigation of early-age cracking of high-performance concrete bridge decks[J]. Construction and Building Materials, 2011, 25 (1): 1-13.
    [123]
    HASHOLT M T, JENSEN O M, KOVLER K, et al. Can superabsorent polymers mitigate autogenous shrinkage of internally cured concrete without compromising the strength?[J]. Construction and Building Materials, 2012, 31: 226-230.
    [124]
    DUDZIAK L, MECHTCHERINE V. Enhancing early-age resistance to cracking in high-strength cement-based materials by means of internal curing using super absorbent polymers[C]//BRAMESHUBER W. 2010Proceedings of the International RILEM Conference on Material Science. New York: Curran Associates, Inc., 2010: 129-139.
    [125]
    SOLIMAN A M, NEHDI M L. Effect of partially hydrated cementitious materials and superabsorbent polymer on earlyage shrinkage of UHPC[J]. Construction and Building Materials, 2013, 41: 270-275.
    [126]
    SUZUKI M, MEDDAH M S, SATO R, et al. Long-term shrinkage and stress in ultra high strength concrete using porous ceramic waste for internal curing[C]//Curran Associates. International RILEM Conference on Use of Superabsorbent Polymers and Other New Additives in Concrete. New York: Curran Associates, Inc., 2010: 5-7.
    [127]
    WANG Chong, YANG Chang-hui, LIU Fang, et al. Preparation of ultra-high performance concrete with common technology and materials[J]. Cement and Concrete Composites, 2012, 34 (4): 538-544.
    [128]
    HAJAR Z, LECOINTRE D, SIMON A, et al. Design and construction of the world first ultra-high performance concrete road bridges[C]//SCHMIDT M, FEHLING E, GEISENHANSLÜKE C. 1st International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2004: 39-48.
    [129]
    THIBAUX T. UHPFRC prestressed beams as an alternative to composite steel-concrete decks: the example of Pinel Bridge[C]//WALRAVEN J C, STOELHORST D. 2008International FIB Symposium on Tailor Made Concrete Structures. Boca Raton: CRC Press, 2008: 1077-1083.
    [130]
    MA Jian-xin, ORGASS M, DEHN F, et al. Comparative investigations on ultra-high performance concrete with and without coarse aggregates[C]//SCHMIDT M, FEHLING E, GEISENHANSLÜKE C. 1st International Symposium on Ultra High Performance Concrete. Kassel: Kassel University Press, 2004: 205-212.
    [131]
    SCHEFFLER B, SCHMIDT M. Application of UHPC for multifunctional road pavements[C]//SCHMIDT M, FEHLING E, GLOTZBACH C, et al. 3rd International Symposium on UHPC and Nanotechnology for High Performance Construction Materials. Kassel: Kassel University Press, 2012: 913-920.
    [132]
    程俊, 刘加平, 刘建忠, 等. 含粗骨料超高性能混凝土力学性能研究及机理分析[J]. 材料导报, 2017, 31 (12): 115-119, 131. https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201723017.htm

    CHENG Jun, LIU Jia-ping, LIU Jian-zhong, et al. An experimental study and a mechanism analysis on mechanical properties of ultra-high performance concrete with coarse aggregate[J]. Materials Review, 2017, 31 (12): 115-119, 131. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201723017.htm
    [133]
    张丽辉, 刘加平, 周华新, 等. 粗骨料与钢纤维对超高性能混凝土单轴拉伸性能的影响[J]. 材料导报, 2017, 31 (12): 109-114. https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201723016.htm

    ZHANG Li-hui, LIU Jia-ping, ZHOU Hua-xin, et al. Effects of coarse aggregate and steel fiber on uniaxial tensile property of ultra-high performance concrete[J]. Materials Review, 2017, 31 (12): 109-114. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-CLDB201723016.htm
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索

    Article Metrics

    Article views (2055) PDF downloads(1045) Cited by()