Mechanics characteristics of surface damage on sliding-rolling friction pair under high-speed and heavy-load condition(PDF)

《交通运输工程学报》[ISSN:1671-1637/CN:61-1369/U]

Issue:
2017年03期
Page:
75-82
Research Field:
载运工具运用工程
Publishing date:
2017-08-05

Info

Title:
Mechanics characteristics of surface damage on sliding-rolling friction pair under high-speed and heavy-load condition
Author(s):
PENG Bo1 KONG Wen-qin1 JIA Lei1 LI Yong-jun1 WANG Li- qin2
1. Research and Development Center, China Academy of Launch Vehicle Technology, Beijing 100076, China; 2. School of Mechatronics Engineering, Harbin Institute of Technology, Harbin 150001, Heilongjiang, China
Keywords:
sliding-rolling friction pair surface damage finite element analysis mechanical characteristics plastic strain
PACS:
V233.45
DOI:
-
Abstract:
An elasto-plastic contact model of M50 steel sliding-rolling friction pair was built by using the finite element method. Under the high-speed and heavy-load condition that the contact stress was about 4.0 GPa and the velocity was about 50 m·s-1, the Von Mises stress, shear stress and plastic deformation of surface layer were analyzed, the effects of the friction coefficient and the relative sliding velocity on the contact behaviors of the M50 steel sliding-rolling friction pair were studied, and the plastic deformations of surface layers were compared in M50 steel double-roller sliding-rolling test result. Calculation result shows that the differences of maximum contact stresses and major and minor axis lengths of elliptical contact region between the finite element analysis result and the Hertz theory calculation result are 2.66%, 0.26% and 6.43%, respectively. When the friction coefficient increases from 0.1 to 0.5, the location of maximum Von Mises stress gradually moves from the friction pair subsurface at about 0.5 mm to the contact surface. When the scuffing failure of friction pair surface occurs, the friction coefficient is more than 0.3, and the maximum Von Mises stress is over 1 700 MPa. When the scuffing failure occurs, the stress and plastic strain of M50 steel friction pair have specific direction. Under the condition that sliding-rolling ratios are 0.12 and 0.15, respectively, the maximum Von Mises stresses are 2 847 MPa and 2 689 MPa on the contact point with higher linear velocity, which leads to relatively large plastic strain, and the maximum values are 0.062 and 0.061, respectively. However, on the surface with lower linear velocity at the two sliding-rolling ratios, the maximum Von Mises stresses are 2 269 MPa and 2 101 MPa, respectively, the plastic strains are smaller, and the maximum values are 0.040 and 0.039, respectively. 3 tabs, 11 figs, 25 refs.

References:

[1] EBERT F J. An overview of performance characteristics, experiences and trends of aerospace engine bearings technologies[J]. Chinese Journal of Aeronautics, 2007, 20(4): 378-384.
[2] 徐流杰,魏世钟,张永振,等.轧辊用高钒高速钢的滚-滑动磨损性能及失效行为研究[J].摩擦学学报,2009,29(1):55-60. XU Liu-jie, WEI Shi-zhong, ZHANG Yong-zhen, et al. Rolling/sliding wear property and failure behavior of high- vanadium high-speed steel for rolls[J]. Tribology, 2009, 29(1): 55-60.(in Chinese)
[3] SILAEV B M, FEDOROV D G, DANILENKO P A. Dynamic of damage of aircraft engine high-speed rolling-element bearings tested in low-viscosity model mediums[J]. Procedia Engineering, 2017, 176: 43-49.
[4] SILAEV B M, DANILENKO P A. Architecture of a multifactor conceptual model of high-speed rolling-contact bearing for aircraft engines and research guidelines[J]. Russian Aeronautics, 2014, 57(4): 416-420.
[5] WANG L, WOOD R J K.The influence of contact conditions on surface reaction layers formed between steel surfaces lubricated by an aviation oil[J]. Tribology International, 2007, 40(10-12): 1655-1666.
[6] INGRAM M, HAMER C, SPIKES H. A new scuffing test using contra-rotation[J]. Wear, 2015, 328-329: 229-240.
[7] FAN Jing-yun, SPIKES H. New test for mild lubricated wear in rolling-sliding contacts[J]. Tribology Transactions, 2007, 50(2): 145-153.
[8] WOJCIECHOWSKI , EYMARD S, IGNASZAK Z, et al. Fundamentals of ductile cast iron scuffing at the boundary lubrication regime[J]. Tribology International, 2015, 90: 445-454.
[9] ZENG Dong-fang, LU Liao-tao, ZHANG Ning, et al. Influence of a hybrid treatment consisting of fine particle bombardment and powder impact plating on the scuffing behavior of ductile cast iron[J]. Wear, 2017, 372-373: 1-11.
[10] SAVOLAINEN M, LEHTOVAARA A. An experimental approach for investigating scuffing initiation due to overload cycles with a twin-disc test device[J]. Tribology International, 2017, 109: 311-318.
[11] QUILLIEN M, GRAS R, COLLONGEAT L, et al. A testing device for rolling-sliding behavior in harsh environments: the twin-diskcryotribometer[J]. Tribology International, 2001, 34(4): 287-292.
[12] SNIDLE R W, DHULIPALLA A K, EVANS H P. Scuffing performance of a hard coating under EHL conditions at sliding speeds up to 16 m/s and contact pressures up to 2.0 GPa[C]∥ASME. 10th International Power Transmission and Gearing Conference. New York: ASME, 2007: 697-715.
[13] MBAREK M, RHAIEM S, KHARRAT M, et al. Experimental study of the rolling-sliding contact conditions in a PA66/steel gear using twin-disc test rig: friction and wear analysis [J]. Surface Review and Letters, 2015, 22(6): 1-11.
[14] ROSADO L, FORSRER N H, Thompson K L, et al. Rolling contact fatigue life and spall propagation of AISI M50, M50NiL, and AISI 52100, Part I: experimental results[J]. Tribology Transactions, 2010, 53(1): 29-41.
[15] FORSTER N E, ROSADO L, OGDEN W P, et al. Rollingcontact fatigue life and spall propagation of AISI M50, M50NiL, and AISI 52100, Part III: metallurgical examination[J]. Tribology Transactions, 2010, 53(1): 52-59.
[16] BHATTACHARYYA A, SUBHASH G, ARAKERE N, et al. Influence of residual stress and temperature on the cyclic hardening response of M50 high-strength bearing steel subjected to rolling contact fatigue[J]. Journal of Engineering Materials and Technology, 2016, 138(2): 1-51.
[17] CENTO P, DAREING D W. Ceramic materials in hybrid ball bearings[J]. Tribology Transactions, 1999, 42(4): 707 -714.
[18] HAGER JR C H, DOLL G L, EVANS R D, et al. Minimum quantity lubrication of M50/M50 and M50/Si3N4 tribological interfaces[J]. Wear, 2011, 271(9/10): 1761-1771.
[19] 刘佐民.M50高速钢高温摩擦磨损特性的研究[J].摩擦学学报,1997,17(1):38-44. LIUZuo-min. Friction and wear characteristics of M50 high speed steel at elevated temperature[J]. Tribology, 1997, 17(1): 38-44.(in Chinese)
[20] NÉLIAS D, DUMONT M L, COUHIER F, et al. Experimental and theoretical investigation on rolling contact fatigue of 52 100 and M50 steels under EHL or Micro-EHL conditions[C]∥ASME. Proceedings of the 1997 Joint ASME/STLE/IMechE World Tribology Conference. New York: ASME, 1997: 184-190.
[21] WANG Li-qin, PENG Bo, GU Le, et al. Tribological Performance of M50 steel tribo-parts[J]. Tribology Transactions, 2012, 55(2): 191-198.
[22] PENG Bo, WANG Li-qin, FAN Shou-xiao, et al. A two-disk test rig for researching the damage behavior of rolling/sliding contact surfaces under extreme conditions[J]. Advanced Materials Research, 2011, 291-294: 1500- 1505.
[23] AL-HAMOOD A, CLARKEL A, EVANS H P. Experimental determination of heat partition in elastohydrodynamic contacts[J]. Proceedings of the Institution of Mechanical Engineers, Part J: Journal of Engineering Tribology, 2015, 229(8): 940-949.
[24] BOBZIN K, BRÖGELMANN T, STAHL K, et al. Friction reduction of highly-loaded rolling-sliding contacts by surface modifications under elasto-hydrodynamic lubrication[J]. Wear, 2015, 328-329: 217-228.
[25] BREWE D E, HAMROCK B J. Simplified solution for elliptical-contact deformation between two elastic solids [J].Journal of Lubrication Technology, 1977, 99(4): 405-409.

Memo

Memo:
-
Last Update: 2017-08-05