Analysis on rail wear and crack initiation and recommendation on rail selection in urban rail transit
Article Text (Baidu Translation)
-
摘要: 分析了基于能量密度法和临界平面法的滚动接触疲劳裂纹萌生预测理论与Archard法的磨耗预测理论, 提出了城市轨道交通钢轨滚动接触疲劳裂纹萌生和磨耗共存发展预测模型; 针对城市轨道交通常用的U71Mn热轧、U75V热轧和U75V热处理等3种不同硬度的钢轨, 预测其表面滚动接触疲劳裂纹的萌生寿命、相应的钢轨型面变化和磨耗发展率; 分析了3种硬度钢轨的疲劳裂纹萌生和磨耗发展特征; 基于安定极限理论, 结合城市轨道交通常见坡度和常用ER9型车轮, 从轮轨硬度匹配的角度提出了城市轨道交通的钢轨选型建议。研究结果表明: 随着硬度的增大, 钢轨滚动接触疲劳裂纹萌生寿命延长, 磨耗发展率降低, U75V热轧和U75V热处理钢轨的磨耗发展率分别比U71Mn热轧钢轨低3.2%和12.1%, 裂纹萌生寿命分别比U71Mn延长14.8%和31.1%;在城市轨道交通常用坡度情况下, 3种不同硬度的钢轨材料都处于弹性安定极限范围, 但随着坡度增大, 钢轨材料趋向于塑性安定极限; 考虑与ER9车轮的硬度匹配情况, 建议钢轨踏面较车轮踏面的硬度高些, ER9车轮与U75V热轧钢轨和U75V热处理钢轨的轮轨硬度比分别为0.87~1.04和0.71~0.84, 这2种钢轨均适合于中国的城市轨道交通系统。Abstract: The theory of rolling contact fatigue (RCF) crack prediction based on the energy density method and critical plane method, and wear prediction theory based on the Archard method were analyzed, aprediction model of the coexistence of RCF crack initiation and wear growth in rails of urban rail transit (URT) was presented. The RCF crack initiation life, corresponding rail profile evolution and wear growth rate were predicted for three kinds of the rails with different hardnesses, named U71 Mn as-rolled, U75 Vas-rolled, and U75 Vheat-treated rails that were commonly used in URT. The development characteristics of the fatigue crack initiation and wear growth were analyzed. Based on the shakedown limit theory, according to the common gradients and type ER9 wheel, the rail selection suggestion for URT was proposed considering the hardness match between the wheel and rail. Analysis result shows that the RCFcrack initiation lifes of the rails prolong and the wear growth rates reduce with the increase of the rail hardness. Compared with those of U71 Mn as-rolled rail, the wear growth rates of the U75 V as-rolled and heat-treated rails reduce by 3.2% and 12.1%, respectively, and their crack initiation lifes prolong by 14.8% and 31.1% respectively. The materials of three kinds of rails with different hardnesses are all within the elastic shakedown limit under the common gradients condition in URT, but they will tend to the plastic shakedown limit with the increase of the gradient. Given the hardness match of the ER9 wheel, it is recommended that the hardness of the rail surface should be higher than that of the wheel tread. The wheel-rail hardness ratios are 0.87-1.04 for U75 Vas-rolled rail and ER9 wheel, and 0.71-0.84 for U75 Vheat-treated rail and ER9 wheel, respectively. Both U75 Vrails can be adapted to the URT system in China.
-
Key words:
- urban rail transit /
- rail /
- rolling contact fatigue /
- wear /
- wheel-rail hardness match
-
图 3 U75V热处理钢轨在裂纹萌生前的磨耗型面发展
Figure 3. Worn profile evolution of U75Vheat-treated rail before crack initiation
图 4 三种钢轨在不同磨耗型面发展阶段时的磨耗发展率
Figure 4. Wear growth rates of three kinds of rails at different worn profile evolution phases
图 8 不同坡度条件下3种钢轨材料的安定极限
Figure 8. Material shakedown limits of three kinds of rails with different gradients
表 2 三种钢轨的平均磨耗发展率和疲劳裂纹萌生寿命
Table 2. Average wear growth rates and fatigue crack initiation lifes of three kinds of rails
下载: 导出CSV
-
[1] KALOUSEK J, MAGEL E. Achieving a balance: the"magic"wear rate[J]. Railway Track and Structures, 1997, 95 (5): 50-53. [2] MAGEL E, RONEY M, KALOUSEK J, et al. The blending of theory and practice in modern rail grinding[J]. Fatigue and Fracture of Engineering Materials and Structures, 2003, 26 (10): 921-929. doi: 10.1046/j.1460-2695.2003.00669.x [3] ZHOU Yu, WANG Shao-feng, WANG Tian-yi, et al. Field and laboratory investigation of the relationship between rail head check and wear in a heavy-haul railway[J]. Wear, 2014, 315 (1/2): 68-77. [4] FLETCHER D I, BEYNON J H. Equilibrium of crack growth and wear rates during unlubricated rolling-sliding contact of pearlitic rail steel[J]. Proceedings of the Institution of Mechanical Engineers, Part F: Journal of Rail and Rapid Transit, 2000, 214 (2): 93-105. doi: 10.1243/0954409001531360 [5] ZHONG W, HU J J, SHEN P, et al. Experimental investigation between rolling contact fatigue and wear of high-speed and heavy-haul railway and selection of rail material[J]. Wear, 2011, 271 (9/10): 2485-2493. [6] FRANKLIN F J, WIDIYARTA I, KAPOOR A. Computer simulation of wear and rolling contact fatigue[J]. Wear, 2001, 251 (1-12): 949-955. doi: 10.1016/S0043-1648(01)00732-3 [7] FRANKLIN F J, CHUNG T, KAPOOR A. Ratcheting and fatigue-led wear in rail-wheel contact[J]. Fatigue and Fracture of Engineering Materials and Structures, 2003, 26 (10): 949-955. doi: 10.1046/j.1460-2695.2003.00703.x [8] ALWAHDI F, FRANKLIN F J, KAPOOR A. The effect of partial slip on the wear rate of rails[J]. Wear, 2005, 258 (7/8): 1031-1037. [9] FRANKLIN F J, GARNHAM J E, FLETCHER D I, et al. Modelling rail steel microstructure and its effect on crack initiation[J]. Wear, 2008, 265 (9/10): 1332-1341. [10] WIDIYARTA I M, FRANKLIN F J, KAPOOR A. Modelling thermal effects in ratcheting-led wear and rolling contact fatigue[J]. Wear, 2008, 265 (9/10): 1325-1331. [11] TRUMMER G, MARTE C, DIETMAIER P, et al. Modeling surface rolling contact fatigue crack initiation taking severe plastic shear deformation into account[J]. Wear, 2016, 352/353: 136-145. doi: 10.1016/j.wear.2016.02.008 [12] TRUMMER G, MARTE C, SCHERIAU S, et al. Modeling wear and rolling contact fatigue: parametric study and experimental results[J]. Wear, 2016, 366/367: 71-77. doi: 10.1016/j.wear.2016.04.024 [13] DAVES W, KUBIN W, SCHERIAU S, et al. A finite element model to simulate the physical mechanisms of wear and crack initiation in wheel/rail contact[J]. Wear, 2016, 366/367: 78-83. doi: 10.1016/j.wear.2016.05.027 [14] DIRKS B, ENBLOM R. Prediction model for wheel profile wear and rolling contact fatigue[J]. Wear, 2011, 271 (1/2): 210-217. [15] ZHOU Yu, HAN Yan-bin, MU Dong-sheng, et al. Prediction of the coexistence of rail head check initiation and wear growth[J]. International Journal of Fatigue, 2018, 112: 289-300. doi: 10.1016/j.ijfatigue.2018.03.027 [16] 李伟, 曾全君, 朱士友, 等. 地铁钢轨波磨对车辆和轨道动态行为的影响[J]. 交通运输工程学报, 2015, 15 (1): 34-42. doi: 10.19818/j.cnki.1671-1637.2015.01.005LI Wei, ZENG Quan-jun, ZHU Shi-you, et al. Effect of metro rail corrugation on dynamic behaviors of vehicle and track[J]. Journal of Traffic and Transportation Engineering, 2015, 15 (1): 34-42. (in Chinese). doi: 10.19818/j.cnki.1671-1637.2015.01.005 [17] 刘洋, 蒋硕, 吴亚平, 等. 剥离掉块对轮轨滑动接触热弹塑性的影响[J]. 交通运输工程学报, 2016, 16 (2): 46-55. http://transport.chd.edu.cn/article/id/201602006LIU Yang, JIANG Shuo, WU Ya-ping, et al. Effects of spallation on rail thermo-elasto-plasticity in wheel-rail sliding contact[J]. Journal of Traffic and Transportation Engineering, 2016, 16 (2): 46-55. (in Chinese). http://transport.chd.edu.cn/article/id/201602006 [18] ZHOU Yu, YU Miao, JIANG Jun-nan. Effects of rail hardness on rail wear and head check initiation[J]. Transportation Research Record, 2016 (2545): 55-65. [19] 周宇, 张杰, 王少峰, 等. 考虑磨耗的钢轨疲劳裂纹萌生寿命预测仿真[J]. 铁道学报, 2016, 38 (7): 91-97. https://www.cnki.com.cn/Article/CJFDTOTAL-TDXB201607013.htmZHOU Yu, ZHANG Jie, WANG Shao-feng, et al. Simulation on rail head check initiation life prediction considering rail wear[J]. Journal of the China Railway Society, 2016, 38 (7): 91-97. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-TDXB201607013.htm [20] KALKER J J. A fast algorithm for the simplified theory of rolling contact[J]. Vehicle System Dynamics, 1982, 11 (1): 1-13. doi: 10.1080/00423118208968684 [21] DEARIZON J, VERLINDEN O, DEHOMBREUX P. Prediction of wheel wear in urban railway transport: comparison of existing models[J]. Vehicle System Dynamics, 2007, 45 (9): 849-866. doi: 10.1080/00423110601149335 [22] AKAMA M. Development of finite element model for analysis of rolling contact fatigue cracks in wheel/rail systems[J]. Quarterly Report of RTRI, 2007, 48 (1): 8-14. doi: 10.2219/rtriqr.48.8 [23] ONALO, CANADINCD, SEHITOGLUH, etal. Investigation of rolling contact crack initiation in bainitic and pearlitic rail steels[J]. Fatigue and Fracture of Engineering Materials and Structures, 2012, 35 (11): 985-997. doi: 10.1111/j.1460-2695.2012.01686.x [24] MINER M A. Cumulative damage in fatigue[J]. Applied Mechanics—Transactions of the ASME, 1945, 13 (3): 159-164. [25] 曾向荣, 张格妍, 赵晓华. 关于城市轨道交通钢轨选型的探讨和建议[J]. 都市快轨交通, 2007, 20 (2): 51-54. https://www.cnki.com.cn/Article/CJFDTOTAL-DSKG200702013.htmZENG Xiang-rong, ZHANG Ge-yan, ZHAO Xiao-hua. Analysis and proposals on rail type selection for urban rail transit[J]. Urban Rapid Rail Transit, 2007, 20 (2): 51-54. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-DSKG200702013.htm [26] 金伟, 栾治国, 刘小松. 杭州地铁1号线项目的轮轨硬度匹配及车轮材质选用[J]. 铁道车辆, 2012, 50 (7): 27-30. https://www.cnki.com.cn/Article/CJFDTOTAL-TDCL201207010.htmJIN Wei, LUAN Zhi-guo, LIU Xiao-song. The wheel-rail hardness matching and wheel material selection for the project of Hangzhou Metro No. 1Line[J]. Rolling Stock, 2012, 50 (7): 27-30. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-TDCL201207010.htm -
点击查看大图
图(8) / 表(2)
计量
- 文章访问数: 1077
- HTML全文浏览量: 274
- PDF下载量: 451
- 被引次数: 0