沥青混合料密实性能

Densification of Asphalt Mixture

摘要: 通过Superpave旋转压实仪SGC, 可以获知室内压实试件在压实过程中高度的精确变化, 进而得到室内试件的整个密实过程。SGC密实曲线提供了混合料密实过程的内在特性, 这一信息与室外交通荷载对混合料的密实具有同样的价值。分析了Superpave旋转压实仪SGC有关密实曲线斜率, 并对密实能量指数能否反映混合料的压实性能提出质疑
- 沥青混合料 /
- 旋转压实仪 /
- 压实能指数 /
- 密实曲线斜率 /
- 交通密实指数
Abstract: With the help of Superpave Gyratory Compactor, the data about the accurate change of asphalt mixture in height during the compaction in the lab, and the densification curve of test are derived. The curve can provide the inherent characteristics.The information has the same value as the densification characteristics under the traffic loads. The results indicated from the densification curves are analyzed, and whether the densification energy index can reflect the mixture's densification is questioned.
- asphalt mixture /
- Superpave Gyratory Compactor /
- construction engergy index /
- densification curve /
- traffic densification index

图 1 常规坐标中混合料M₁和M₂在最大压实次数下的密实曲线

下载: 全尺寸图片幻灯片

图 2 半对数坐标图上混合料M₁和M₂在最大压实次数下的密实曲线

下载: 全尺寸图片幻灯片

图 3 混合料M₁和M₂在N_des-N_max间的密实曲线

下载: 全尺寸图片幻灯片

图 4 密实度能量指数CEI、TDI96、TDI98示意图

下载: 全尺寸图片幻灯片

图 5 密实度曲线斜率和曲线下面积示意图

下载: 全尺寸图片幻灯片

表 1 Superpave法体积参数

压实次数	级配类型	沥青用量	体积参数
压实次数	级配类型	沥青用量	G_mm1/%	G_mm2/%	Va%	VMA%	VFA%
N_max=160	M₁	4.7	85.8	95.8	4.2	15.5	72.9
N_max=160	M₂	5.2	85.7	96.0	4.0	16.0	75.0
注: 表中G_mm1、G_mm2分别为沥青混合料在旋转压实次数N_ini、N_des下的相对密实度。

下载: 导出CSV

表 2 Superpave密实特性

下载: 导出CSV

[1]	袁迎捷. Superpave沥青混合料设计方法与压实原理研究[D]. 西安: 长安大学, 2001.
[2]	RAJIB B Mallick. Use of superpave gyratory comp-actor to characterise hot mix asphalt (HMA) [A]. TRB. The 1999 Anual Meeting of the Transportation Research Board[C]. Washington. D C, 1999.