摘要: 为了有效评价集料表面纹理粗糙程度对沥青混合料路用性能的影响, 采用激光轮廓仪直接测量了9种不同集料的表面纹理轮廓曲线, 通过轮廓滤波方法将其划分为宏观纹理和微观纹理, 并应用几何统计方法, 以算术平均偏差、算术平均波长和轮廓偏斜度为评价指标, 对其表面纹理粗糙度进行了定量评定。分析结果表明: 算术平均偏差最适宜用来描述集料表面纹理的粗糙程度, 算术平均偏差越大, 集料表面纹理的粗糙度越大; 波长2mm为集料表面宏观纹理和微观纹理的界限值; 根据算术平均偏差, 集料表面纹理粗糙度可以划分为4级。Abstract: In order to effectively evaluate the remarkably influence of the roughness of aggregate surface texture on the pavement performance of asphalt mixture, nine different aggregate surface textures were measured directly by using laser profilometer, then the textures were divided into micro-textures and macro-textures by using profile filter method. Geometry statistical method was adopted to evaluate the roughnesses of the textures quantitatively. The evaluation indexes were arithmetic mean deviation, arithmetic mean wavelength and outline skewness. Evaluation result indicates that arithmetic mean deviation is the most conformable index to describe the roughness of aggregate surface texture. Moreover, with the increase of arithmetic mean deviation, the roughness of aggregate surface texture change larger. Aggregate surface textures are divided into macro-textures and micro-textures according to 2 mm wavelength limit. The roughnesses of aggregate surface textures can be classified into four different grades according to arithmetic mean deviation.
-
表 1 集料种类和来源
Table 1. Sources and kinds of aggregates
集料品种 唐山白色花岗岩 唐山红色花岗岩 吉林玄武岩 河北玄武岩 哈尔滨玄武岩 新疆红色玄武岩 新疆灰色玄武岩 吉林石灰岩 辽宁石灰岩 编号 A B C D E F G H I 
下载: 导出CSV
表 2 集料表面纹理粗糙度分类结果
Table 2. Classifing result of roughnesses of aggregate surface textures
等级 1 2 3 4 集料 A、B C、D F、G、H、I E 特性描述 非常粗糙 粗糙 光滑 非常光滑 算术平均偏差Ra/μm > 200 120~200 70~120 < 70
下载: 导出CSV
-
[1] 黄宝涛, 梁轶, 崔娥, 等. 沥青混合料抗车辙性能的分形描述方法[J]. 交通运输工程学报, 2007, 7(6): 59-63. http://transport.chd.edu.cn/article/id/200706012HUANG Bao-tao, LI ANG Yi, CUI E. Fractal description method of asphalt mixture rut resistance[J]. Journal of Traffic and Transportation Engineering, 2007, 7(6): 59-63. (in Chinese) http://transport.chd.edu.cn/article/id/200706012 [2] KANDHAL P S. Evaluation of asphalt absorption by mineral aggregates[J]. Journal of the Association of Asphalt Paving Technologists, 1991, 60(1): 207-208. [3] 陈国明, 谭忆秋, 王哲人, 等. 集料表面纹理测量的试验设计[J]. 中国公路学报, 2006, 19(2): 36-41. https://www.cnki.com.cn/Article/CJFDTOTAL-ZGGL200602006.htmCHEN Guo-ming, TAN Yi-qiu, WANG Zhe-ren, et al. Experi mental design for measurement on aggregates surface texture[J]. China Journal of Highway and Transport, 2006, 19(2): 36-41. (in Chinese) https://www.cnki.com.cn/Article/CJFDTOTAL-ZGGL200602006.htm [4] 李强, 马松林, 王鹏飞. 沥青路面冷再生混合料疲劳性能[J]. 交通运输工程学报, 2004, 4(1): 7-10. doi: 10.3321/j.issn:1671-1637.2004.01.003LI Qiang, MASong-lin, WANG Peng-fei. Fatigue properties of cold recycled asphalt mixture[J]. Journal of Traffic and Transportation Engineering, 2004, 4(1): 7-10. (in Chinese) doi: 10.3321/j.issn:1671-1637.2004.01.003 [5] 吴启宏. 集料对沥青混合料路面车辙的影响[J]. 国外公路, 1998(1): 43-47. https://www.cnki.com.cn/Article/CJFDTOTAL-QHKJ201502019.htmWU Qi-hong. The influence of hot mixed asphalt on pavement wheel rutting[J]. Foreign Highway, 1998(1): 43-47. (in Chinese) https://www.cnki.com.cn/Article/CJFDTOTAL-QHKJ201502019.htm [6] 王政平, 张锡芳, 张艳娥. 表面粗糙度光学测量方法研究进展[J]. 传感器与微系统, 2007, 26(9): 4-6. doi: 10.3969/j.issn.1000-9787.2007.09.002WANG Zheng-ping, ZHANG Xi-fang, ZHANG Yan-e. Progress on optical measurement of surface roughness[J]. Transducer and Microsystem Technologies, 2007, 26(9): 4-6. (in Chinese) doi: 10.3969/j.issn.1000-9787.2007.09.002 [7] 向红军, 雷彬. 表面粗糙度测试仪中光纤传感器的设计[J]. 传感技术学报, 2007, 20(3): 645-648. https://www.cnki.com.cn/Article/CJFDTOTAL-CGJS200703016.htmXI ANG Hong-jun, LEI Bin. Design of fiber optic sensor in rough meter[J]. Chinese Journal of Sensors and Actuators, 2007, 20(3): 645-648. (in Chinese) https://www.cnki.com.cn/Article/CJFDTOTAL-CGJS200703016.htm [8] 许景波, 袁怡宝, 朴伟英, 等. 减小表面粗糙度测量高斯滤波幅度偏差[J]. 机械工程学报, 2006, 42(4): 42-46. https://www.cnki.com.cn/Article/CJFDTOTAL-JXXB200604008.htmXUJing-bo, YUAN Yi-bao, PI AO Wei-ying. Decreasing the amplitude characteristic deviation of gaussian filter in surface roughness measurements[J]. Chinese Journal of Mechanical Engineering, 2006, 42(4): 42-46. (in Chinese) https://www.cnki.com.cn/Article/CJFDTOTAL-JXXB200604008.htm [9] 胡涛. 用于汽轮机动静间隙检测的激光光纤传感技术研究[D]. 哈尔滨: 哈尔滨工业大学, 2001. [10] 马惠萍, 刘丽华, 杨乐民, 等. 用于燃气轮机动态间隙检测的关键技术研究[J]. 光电子激光, 2002, 13(3): 270-273. https://www.cnki.com.cn/Article/CJFDTOTAL-GDZJ200203014.htmMA Hui-ping, LIULi-hua, YANG Le-min, et al. Study on key technology on testing dynamic clearance of gas turbine[J]. Photoelectron and Laser, 2002, 13(3): 270-273. (in Chinese) https://www.cnki.com.cn/Article/CJFDTOTAL-GDZJ200203014.htm [11] 王建军, 徐西鹏. 花岗石抛光表面的粗糙度、分形维数及其关系研究[J]. 计量学报, 2007, 28(2): 520-524. https://www.cnki.com.cn/Article/CJFDTOTAL-JLXB200702006.htmWANG Jian-jun, XU Xi-peng. Roughness and fractal di mension of polished granite surfaceand their relationship[J]. ACTA Metrologica Sinica, 2007, 28(2): 520-524. (in Chinese) https://www.cnki.com.cn/Article/CJFDTOTAL-JLXB200702006.htm [12] 袁怡宝. 表面轮廓信号的数字滤波及表征参数计算方法的研究[D]. 哈尔滨: 哈尔滨工业大学, 1987. [13] 陈国明. 沥青混合料中粗集料表面物理特性的研究[D]. 哈尔滨: 哈尔滨工业大学, 2005. -
点击查看大图
图(16) / 表(2)
计量
- 文章访问数: 448
- HTML全文浏览量: 192
- PDF下载量: 357
- 被引次数: 0