温拌SBS沥青混合料旋转压实特性

ZHANG Jiu-peng; PEI Jian-zhong; XU Li; XING Xiang-yang

doi:10.19818/j.cnki.1671-1637.2011.01.001

温拌SBS沥青混合料旋转压实特性

doi: 10.19818/j.cnki.1671-1637.2011.01.001

1.
长安大学特殊地区公路工程教育部重点实验室，陕西西安 710064
2.
中交第一公路勘察设计研究院有限公司，陕西西安 710075

基金项目:

China Postdoctoral Science Foundation 20100481312

Special Fund for Basic Scientific Research of Central Colleges, Chang'an University CHD2009JC069

New Century Excellent Talents in University NCET-07-0120

详细信息

中图分类号: U414.75
计量
- 文章访问数: 756
- HTML全文浏览量: 128
- PDF下载量: 412
- 被引次数: 0
出版历程
- 收稿日期: 2010-07-21
- 刊出日期: 2011-02-25

Gyratory compaction characteristic of SBS warm mixed asphalt mixture

1.
Key Laboratory for Special Area Highway Engineering of Ministry of Education, Chang'an University, Xi'an 710064, Shaanxi, China
2.
CCCC First Highway Consultants Co., Ltd., Xi'an 710075, Shaanxi, China

Funds:

China Postdoctoral Science Foundation 20100481312

Special Fund for Basic Scientific Research of Central Colleges, Chang'an University CHD2009JC069

New Century Excellent Talents in University NCET-07-0120

More Information

Author Bio:
ZHANG Jiu-peng(1983-), Male, Yancheng, Jiangsu, Lecturer of Chang'an University, PhD, Research on the Highway Engineering, +86-29-62630058. zhjiupeng@163.com

摘要

摘要: 采用旋转压实仪(SGC) 成型温拌SBS沥青混合料试件, 根据体积参数的变化规律确定了最佳拌合温度, 根据旋转压实曲线对温拌沥青混合料和热拌沥青混合料的压实特性进行了对比分析。分析结果表明: 与热拌沥青混合料相比, 用旋转压实法确定温拌沥青混合料成型温度降低约20℃, 动稳定度提高30%, 低温抗裂和抗水损害能力相差不大。在压实初期, 热拌沥青混合料SGC压实曲线的斜率为2.53, 密实能量指数为0.246, 温拌沥青混合料SGC压实曲线的斜率为3.14, 密实能量指数为0.156, 表明温拌沥青混合料具有更好的施工和易性; 在压实后期, 热拌沥青混合料SGC压实曲线的斜率为0.019 5, 密实能量指数为1.95和1.65, 温拌沥青混合料SGC压实曲线的斜率为0.015 2, 密实能量指数为2.61和2.00, 表明开放交通后温拌沥青混合料具有更好的抵抗荷载压密的能力。
- 路面工程 /
- 温拌沥青混合料 /
- 压实温度 /
- 密实能量指数
Abstract: Superpave gyratory compacter (SGC) was used to make the specimens of SBS warm mixed asphalt mixture (WMA), and the volume characteristics of WMA were compared with hot mixed asphalt mixture (HMA) to determine the reasonable mixing temperature. Furthermore, the slopes and densification energy indexes of SGC compaction curves were introduced to reflect the inherent compaction characteristics of asphalt mixtures. Analysis result indicates that the determined compaction temperature of WMA is lower than HMA by 20 ℃, the dynamic stability of WMA improves by 30%, but its crack resistance at low temperature and its water stability change a little. In the initial stage, the slope of densification curve of HMA is 2.53, and the densification energy index is 0.246. The slope of densification curve of WMA is 3.14, and the densification energy index is 0.156. The result indicates that WMA has better construction workability. In the later stage, the slope of densification curve of HMA is 0.019 5, and the densification energy indexes are 1.95 and 1.65. The slope of densification curve of WMA is 0.015 2, and the densification energy indexes are 2.61 and 2.00. The result indicates that WMA has better capacity to resist the densification under traffic load.10 tabs, 5 figs, 12 refs.
- pavement engineering /
- warm mixed asphalt mixture /
- compaction temperature /
- densification energy index

HTML全文

Figure 1. Influence of compaction temperatures on porosities of asphalt mixtures

下载: 全尺寸图片幻灯片

Figure 2. Densification curves of HMA and WMA under N_max

下载: 全尺寸图片幻灯片

Figure 3. Densification curves of HMA and WMA in N_des-N_max

下载: 全尺寸图片幻灯片

Figure 4. Densification energy indexes

下载: 全尺寸图片幻灯片

Figure 5. Densification energy characteristics of HMA and WMA

下载: 全尺寸图片幻灯片

Table 1. Densities of limestone aggregates with different sizes

下载: 导出CSV

Table 2. Technical indexes of limestone filler

下载: 导出CSV

Table 3. Technical indexes of SBS modified asphalt

下载: 导出CSV

Table 4. Design gradation of AC-13C mixture

下载: 导出CSV

Table 5. Marshall test results of HMA and WMA

下载: 导出CSV

Table 6. Rutting resistances of HMA and WMA

下载: 导出CSV

Table 7. Water stabilities of HMA and WMA

下载: 导出CSV

Table 8. Crack resistances of HMA and WMA

下载: 导出CSV

Table 9. SGC results of HMA and WMA

下载: 导出CSV

Table 10. Densification characteristics of HMA and WMA

下载: 导出CSV

参考文献(12)

[1]	ZHANG Zhen, LIU Li-ping, TANG Wen. Research on performance of Evotherm warm-mix asphalt[J]. Journal of Building Materials, 2009, 12 (4): 438-441.
[2]	LI Zhong-qiu, MA Jing-kun. In-door experiment on Sasobit modifying additive[J]. Journal of Highway and Transportation Research and Development, 2004, 21 (10): 26-29.
[3]	ZHANG Rui, HUANG Xiao-ming. Performance analysis of asphalt and asphalt mixture with Sasobit[J]. Journal of Traffic and Transportation Engineering, 2007, 7 (4): 54-57. http://transport.chd.edu.cn/article/id/200704012
[4]	GUO Ping, QI Feng, MI Hai-chen. Road performance of warm mix asphalt mixture[J]. Journal of Chang'an University: Natural Science Edition, 2010, 30 (3): 10-13.
[5]	JI Xiao-ping, SUN Yun-long. Experimental research of warm mix asphalt with Sasobit[J]. Journal of Wuhan University of Technology, 2010, 32 (14): 75-78.
[6]	XU Shi-fa, LUO Xiao-hui, SUN Zhong-ge. Performance evaluation and comparison of SBS emulsion warm mixture and hot SBS modified asphalt mixture[J]. Journal of Beijing University of Civil Engineering and Architecture, 2008, 24 (2): 25-29.
[7]	WU Chao-fan, ZENG Meng-lan, WANG Mao-wen, et al. Determination of the mixing and compaction temperature for warm mix asphalt with Sasobit[J]. Journal of Hunan University: Natural Sciences, 2010, 37 (8): 1-5.
[8]	ZHOU Yan, CHEN Shuan-fa, ZHENG Mu-lian, et al. Research on mixing and compaction property of warm mix asphalt[J]. Journal of Wuhan University of Technology, 2010, 32 (1): 61-64.
[9]	LIU Zhi-fei, WU Shao-peng, CHEN Mei-zhu, et al. Status and problems of warm mix asphalt[J]. Journal of Wuhan University of Technology, 2009, 31 (4): 170-173.
[10]	JTGF40—2004, technicalspecificationforconstructionohfighwayasphalt pavements[S].
[11]	GE Zhe-sheng, HUANG Xiao-ming, XU Guo-guang. Evaluation of asphalt-mixture's low-temperature anti-cracking performance by curvature strain energy method[J]. Journal of Southeast University: Natural Science Edition, 2002, 32 (4): 653-655.
[12]	ZHANG Zheng-qi, YUAN Ying-jie, WANG Bing-gang. Information of gyratory compaction densification curve of asphalt mixture andits application[J]. China Journal of Highway and Transport, 2005, 18 (3): 1-6.