Pavement performance analysis of asphalts modified by different types of tourmalines
-
摘要: 选取2种电气石粉和4种电气石负离子粉, 采用熔融共混法制备电气石改性沥青, 进行了针入度、软化点和延度性能测试, 研究了电气石类型及掺量对沥青感温性能、高温性能、低温性能与粘附性等路用性能的影响规律。采用改进弯曲流变试验研究了电气石对沥青低温性能的影响效果, 采用水煮法对电气石改性沥青与集料的粘附性能进行评价, 借助扫描电镜试验、差示扫描热试验、压电性试验和热电性试验分析了电气石对沥青路用性能的改善机理。试验结果表明: 电气石粉改性沥青感温性能随掺量增加先改善后变差, 电气石负离子粉改性沥青感温性能呈现相反的变化规律; 各电气石改性沥青高温性能随掺量增加均不断提高; 电气石粉目数越大, 对沥青路用性能改善效果越好; 电气石负离子粉改性沥青的路用性能随负离子释放量的增大而不断降低; 在相同目数条件下, 电气石负离子粉对沥青性能的改善效果优于电气石粉; 电气石能有效改善沥青的低温性能, 而且能够均匀稳定地分散在沥青中, 与沥青形成稳定整体; 电气石加入到沥青后其电性能仍能正常发挥。可见, 电气石能够显著改善沥青的路用性能。Abstract: Two kinds of tourmaline powders and four kinds of tourmaline anion powders were selected to modify asphalt, and the tourmaline modified asphalt was prepared by using a melting-blending method. The penetration, softening point and ductility were tested, and the effect laws of tourmaline types and mixing amount on asphalt temperature sensitivity, high-temperature and low-temperature properties, adhesion property were studied. The effect of tourmaline on asphalt low-temperature property was studied by using improved bending beam rheometer(BBR) test, and the adhesion property between tourmaline modified asphalt and aggregate was evaluated by using water-boiling method. The improved mechanism of tourmaline on asphalt pavement performance was analyzed by using scanning electron microscope(SEM) test, differential scanning calorimetry(DSC) test, piezoelectric test and thermoelectric test. Analysis result shows that the temperature sensitivity of tourmaline powder modified asphalt improves firstly and then reduces with the increase of mixing amount, and that of tourmaline anion powder modified asphalt shows an opposite law. The high-temperature performances of all tourmaline modified asphalts improve with the increase of mixing amount. The pavement performance of tourmaline powder modified asphalt improves significantly with the increase of tourmaline powder mesh, that of tourmaline anion powder modified asphalt reduces unceasingly with the increase of anion release amount.In the same mesh, the effect of tourmaline anion powder on asphalt pavement performance is better than that of tourmaline powder. Tourmaline can well improve the low-temperature property of tourmaline modified asphalt. Tourmaline can disperse in asphalt uniformly and stably, and can form a stable whole. The electric property of tourmaline can be played fully when tourmaline is added into asphalt.So tourmaline can improve the road performance of asphalt significantly.
-
Key words:
- road material /
- tourmaline modified asphalt /
- pavement performance /
- SEM test /
- DSC test
-
表 1 沥青基本性能
Table 1. Physical properties of asphalt
表 2 低温弯曲流变试验结果
Table 2. Test results of BBR at low temperature
表 3 沥青与集料的粘附性等级
Table 3. Adhesion levels between asphalt and aggregate
表 4 压电性能与热电性能试验结果
Table 4. Test results of piezoelectric properties and thermoelectric properties
-
[1] 刘丽, 李剑, 郝培文, 等. 硅藻土改性沥青胶浆技术性能的评价方法[J]. 长安大学学报: 自然科学版, 2005, 25(3): 23-27. https://www.cnki.com.cn/Article/CJFDTOTAL-XAGL200503007.htmLIU Li, LI Jian, HAO Pei-wen, et al. Evaluation method for property of modified asphalt mortar with diatomite[J]. Journal of Chang'an University: Natural Science Edition, 2005, 25(3): 23-27. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-XAGL200503007.htm [2] 张争奇, 李平, 王秉纲. 纤维和矿粉对沥青胶浆性能的影响[J]. 长安大学学报: 自然科学版, 2005, 25(5): 15-18. doi: 10.3321/j.issn:1671-8879.2005.05.004ZHANG Zheng-qi, LI Ping, WANG Bing-gang. Effect of fiber and mineral filler on asphalt mortar performance[J]. Journal of Chang'an University: Natural Science Edition, 2005, 25(5): 15-18. (in Chinese). doi: 10.3321/j.issn:1671-8879.2005.05.004 [3] 张超, 韩伟华, 马琳. 纤维沥青混合料中纤维最佳用量的确定方法[J]. 长安大学学报: 自然科学版, 2009, 29(2): 9-12. https://www.cnki.com.cn/Article/CJFDTOTAL-XAGL200902005.htmZHANG Chao, HAN Wei-hua, MA Lin. Optimum volume determination method of fiber in asphalt mixture[J]. Journal of Chang'an University: Natural Science Edition, 2009, 29(2): 9-12. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-XAGL200902005.htm [4] 袁文豪, 沙爱民, 胡力群, 等. 水泥、乳化沥青及其用量对水泥-乳化沥青混合料性能的影响[J]. 筑路机械与施工机械化, 2005, 22(1): 32-35. https://www.cnki.com.cn/Article/CJFDTOTAL-ZLJX200501011.htmYUAN Wen-hao, SHA Ai-min, HU Li-qun, et al. Cement, emulsified asphalt and their quantities impact on performance of cement and emulsified asphalt mixture[J]. Road Machinery and Construction Mechanization, 2005, 22(1): 32-35. (inChinese). https://www.cnki.com.cn/Article/CJFDTOTAL-ZLJX200501011.htm [5] 蒋玲. 硅藻精土与SBS改性沥青混合料路用性能比较试验研究[J]. 筑路机械与施工机械化, 2009, 26(11): 57-60. doi: 10.3969/j.issn.1000-033X.2009.11.026JIANG Ling. Comparative experimental study on diatomite and SBS modified asphalt mixture pavement performance[J]. Road Machinery and Construction Mechanization, 2009, 26(11): 57-60. (in Chinese). doi: 10.3969/j.issn.1000-033X.2009.11.026 [6] 姜海涛, 吴少鹏, 况栋梁, 等. 有机化蒙脱土改性沥青老化性能的研究[J]. 武汉理工大学学报, 2007, 29(9): 41-43. https://www.cnki.com.cn/Article/CJFDTOTAL-WHGY200709012.htmJINAG Hai-tao, WU Shao-peng, KUANG Dong-liang, et al. Aging properties of organo-modified montmorillonite modified asphalts[J]. Journal of Wuhan University of Technology, 2007, 29(9): 41-43. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-WHGY200709012.htm [7] 张兴友, 谭忆秋, 王哲人. 白炭黑改性沥青及其混合料的路用性能研究[J]. 公路交通科技, 2005, 22(7): 23-25, 40. https://www.cnki.com.cn/Article/CJFDTOTAL-GLJK200507006.htmZHANG Xing-you, TAN Yi-qiu, WANG Zhe-ren. Study on performance of silica modified asphalt and its mixture[J]. Journal of Highway and Transportation Research and Development, 2005, 22(7): 23-25, 40. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GLJK200507006.htm [8] 王英, 胡兆德, 李鹏, 等. 稀土改性沥青路面低温冷补养护材料探讨[J]. 筑路机械与施工机械化, 2008, 25(12): 23-27. https://www.cnki.com.cn/Article/CJFDTOTAL-ZLJX200812031.htmWANG Ying, HU Zhao-de, LI Peng, et al. Discussion on low-temperature cold reinforcement maintenance material for rare earth modified asphalt pavement[J]. Road Machinery and Construction Mechanization, 2008, 25(12): 23-27. (inChinese). https://www.cnki.com.cn/Article/CJFDTOTAL-ZLJX200812031.htm [9] 李芳芳. 电气石的性质及应用展望[J]. 矿业快报, 2007(3): 10-13. https://www.cnki.com.cn/Article/CJFDTOTAL-KYKB200703003.htmLI Fang-fang. Property of tourmaline and application prospect[J]. Express Information of Mining Industry, 2007(3): 10-13. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-KYKB200703003.htm [10] 莫尊理, 孙豫, 郭瑞斌, 等. 电气石的性能及应用研究进展[J]. 硅酸盐通报, 2011, 30(4): 822-826. https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201104018.htmMO Zun-li, SUN Yu, GUO Rui-bin, et al. Research progress in the performance and application of tourmaline[J]. Bulletin of the Chinese Ceramic Society, 2011, 30(4): 822-826. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT201104018.htm [11] HOANG L H, HIEN N T M, CHEN Xiang-bai, et al. Annealing effect in raman scattering of various types of tourmalines[J]. Journal of Applied Spectroscopy, 2013, 79(6): 881-887. [12] LI Ke-xin, CHEN Tong, YAN Liu-shui, et al. Synthesis of mesoporous graphene and tourmaline comdoped titania com-posites and their photocatalytic activity towards organic pollutant degradation and eutrophic water treatment[J]. Catalysis Communications, 2012, 28(5): 196-201. [13] 陈华鑫, 李宁利, 张争奇, 等. 沥青材料的感温性分析[J]. 长安大学学报: 自然科学版, 2006, 26(1): 8-11. https://www.cnki.com.cn/Article/CJFDTOTAL-XAGL200601001.htmCHEN Hua-xin, LI Ning-li, ZHANG Zheng-qi, et al. Temperature susceptibility analysis of asphalt binders[J]. Journal of Chang'an University: Natural Science Edition, 2006, 26(1): 8-11. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-XAGL200601001.htm [14] 季节, 罗晓辉, 徐世法. Sasobit改性沥青的结构与性能研究[J]. 中国公路学报, 2011, 24(5): 18-25. https://www.cnki.com.cn/Article/CJFDTOTAL-ZGGL201105006.htmJI Jie, LUO Xiao-hui, XU Shi-fa. Study of structure and properties of Sasobit modified asphalt[J]. China Journal of Highway and Transport, 2011, 24(5): 18-25. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-ZGGL201105006.htm [15] 王火明, 王林涛, 魏强. BRA改性沥青及其混合料路用性能[J]. 筑路机械与施工机械化, 2012, 29(2): 27-32. https://www.cnki.com.cn/Article/CJFDTOTAL-ZLJX201202016.htmWANG Huo-ming, WANG Lin-tao, WEI Qiang. Performance of BRA modified asphalt and mixture[J]. Road Machinery and Construction Mechanization, 2012, 29(2): 27-32. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-ZLJX201202016.htm [16] 周新锋, 赵琳娜. 橡胶粉改性沥青在高等级公路中的应用研究[J]. 筑路机械与施工机械化, 2012, 29(1): 57-58, 63. https://www.cnki.com.cn/Article/CJFDTOTAL-ZLJX201201032.htmZHOU Xin-feng, ZHAO Lin-na. Research on application of rubber modified asphalt in high-grade highway[J]. Road Machinery and Construction Mechanization, 2012, 29(1): 57-58, 63. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-ZLJX201201032.htm [17] 展杰, 郝霄鹏, 刘宏, 等. 天然矿物功能晶体材料电气石的研究进展[J]. 功能材料, 2006, 37(4): 524-527. https://www.cnki.com.cn/Article/CJFDTOTAL-GNCL200604003.htmZHAN Jie, HAO Xiao-peng, LIU Hong, et al. Research progress of natural mineral functional crystals-tourmaline[J]. Journal of Functional Materials, 2006, 37(4): 524-527. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GNCL200604003.htm [18] 李雯雯, 张晓晖, 吴瑞华, 等. 不同种属电气石的压电效应及磁学性质的研究[J]. 硅酸盐通报, 2007, 26(6): 1116-1121. https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT200706014.htmLI Wen-wen, ZHANG Xiao-hui, WU Rui-hua, et al. Piezoelectricity and magnetic properties of diverse tourmalines[J]. Bulletin of the Chinese Ceramic Society, 2007, 26(6): 1116-1121. (in Chinese). https://www.cnki.com.cn/Article/CJFDTOTAL-GSYT200706014.htm